Non-stable Sensitive to frost

Sikkens Cetol WP 560

Short description: A translucent water borne base stain, moisture vapour permeable stain for factory application to soft and hard woods.

Characteristics:

Specially formulated for application by dipping or flow-coating. Is microporous Excellent adhesion to timber A first class foundation for various types of decorative coatings. Ensures optimum penetration Waterthinnable and environment friendly A base coat for all Sikkens translucent finishes. Provides limited weather resistance
Solid content: 14% Flash point: > 100 C
Density approx. 1,01 Depending on colour Minimum application temperature !0 C ( substrate, air and material ) Cleaning of equipment: with water Package: 20 ltr 120 ltr

Properties:

Composition Acrylic / Alkyd-resin Hybrid system Drying at 23 C / 50% R.H. Dust dry: After approx. 30 min Sandable: After approx. 4 hrs Recoatable: After approx. 4-6 hrs Drying times can be reduced by the installation of forced drying systems. please consult the Technical services department for recommendations. Practical usage by dipping ml/m_ Depending on application method and wood Practical coverage will be affected by factors such as surface condition, component profile, application method, temperature etc. To assess practical spreading rate, a test should be carried out with the items under the precise working conditions. Advised layer thickness: Dipping: Viscosity Not applicable Package viscosity

Application:

Initial Procedure: Stir thoroughly immediately prior to use. method: Dip/flow-coating, spraying Viscosity: ready to use Spray: Can be sprayed on as a substitute for a dip tank, unthinned. N.B Dip tanks and flow coaters for application of this product should be constructed of stainless steel. Dip tanks should be covered with a tight fitting lid when not in use. Spray table: Airless Air assisted Fluid Pressure Air pressure Nozzle size -

Processing notes

Basic rules The processing of Sikkens Cetol WP 560 can occur via dipping, flooding and brushing. The wood moisture when using Sikkens systems should be between 11 % and 15 %. The selection and use of the paint systems, particularly the shade's, comply with the guidelines of the institute for window techniques in Rosenheim and the federal committee for paint and value protection. Paint systems for joinery 1. Fully finished, stable wood frames Impregnation according to DIN Part 3. Only pine wood. Sikkens Cetol WV 881 (according to EN 152.1, EN 113 and RAL). Sikkens Cetol SV 868 (according to EN 152.1, EN 113 and RAL). Primer Sikkens Cetol WP 560 Midcoat Sikkens Cetol WM 660 or 662 Or Sikkens Cetol WF 750 Or Sikkens Cetol WF 755 Finish Sikkens Cetol WF 750 Or Sikkens Cetol WF 755
2. Semi-stable and none stable wooden elements. If coating these types of constructions, one must be aware of a higher swelling and shrinkage of the wood due to the wood moisture. These type of constructions must be coated in a thin build system. The dry film thickness should not exceed 40m with none stable and- 80m Semi-stable elements. Note: 1 Cover up the paint surface during the installation and plastering of the components. 2 Caution, Only use sticky tapes that are compatible with waterthinnable acrylic coatings. Tapes should be removed within two weeks. Viscosity table depending on temperature. DIN cup 4mm at: 30 C 28 C 26 C 24 C 22 C 20 C 18 C 16 C 14 C 12 C 12 12,5 12,seconds seconds seconds seconds seconds seconds seconds seconds seconds seconds